SIKAFAST-3311AB /12 X 490ML
Sika 530423 SikaFast-3311(AB) ; 12x490ML = 1 Case

SikaFast®-3311 - Fast curing, toughened, low to medium modulus, structural adhesive

PRODUCT BENEFITS

  • Strength development within minutes after application
  • Non-sagging and thixotropic formulation
  • Adhesion to a wide range of substrates without or with limited surface preparation
  • Good strength and impact / peel resistance

Usage

SikaFast®-3311 is a fast curing, flexibilized structural adhesive designed to substitute welding, riveting and other mechanical fastening. SikaFast®-3311 is suitable for high strength fastening of joints on different types of substrates including top coats, metals, and plastics with no or limited surface preparation. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.

Packaging

  • Dual cartridge 490 ml
  • Mixer: Sulzer MixPacTMMFHX 10-18
Properties

SikaFast®-3311 (A)

SikaFast®-3311 (B)

Chemical base

Methacrylate

Color (CQP001-1)

mixed

Milky-white

Blue

Blue

Cure mechanism

Radical polymerization

Density (uncured)

mixed (calculated)

0.96 kg/l (8.0 lb/gal)

1.10 kg/l (9.2 lb/gal)

0.97 kg/l (8.1 lb/gal)

Mixing ratio

by volume

by weight

10 : 1

8.7 : 1

Consistency

Thixotropic paste

Application temperature

10 - 35 °C (50 - 95 °F)

Open time (CQP526-2)

6 minutes A

Peak exotherm time / temperature

12 minutes / 95 °C (203 °F) A

Shore D hardness (CQP023-1 / ISO 48-4)

65

Tensile strength (ASTM D638)

10 MPa (1 450 psi)

E-Modulus (ASTM D638)

elongation 0.1 - 1.0 %

450 MPa (65 ksi)

Tensile lap-shear strength (CQP046-6 / ISO 4587)

15 MPa (2 150 psi)

Service temperature (CQP513-1)

-40 - 80 °C (-40 - 176 °F)

Shelf life

drums / pails / cartridges

9 months B