Sika 3511 SikaFast 3511 Structural Panel Bonding Exterior Adhesive 1:1 Ratio
SikaFast®-3511 - Fast curing, toughened, high strength, structural adhesive
PRODUCT BENEFITS
- Strength development within minutes after application
- Non-sagging and thixotropic formulation
- Adhesion to a wide range of substrates without or with limited surface preparation
- Very good strength and impact / peel resistance
Usage
SikaFast®-3511 is a fast curing, flexibilized structural adhesive designed to substitute welding, riveting and other mechanical fastening. SikaFast®-3511 is suitable for high strength fastening of joints on different types of substrates including top coats, metals, and plastics with no or limited surface preparation. This product is suitable for experienced professional users only. Tests with actual substrates and conditions have to be performed ensuring adhesion and material compatibility.
Packaging
- Dual cartridge 400 ml
- Mixer: Sulzer MFQ 10-24T
| Properties |
| ||||
| Chemical base | Methacrylate | ||||
| Color (CQP001-1) |
mixed |
| |||
| Cure mechanism | Radical polymerization | ||||
| Density (uncured) |
mixed (calculated) |
| |||
| Mixing ratio | by volume by weight | 1 : 1 1 : 1 | |||
| Consistency | Thixotropic paste | ||||
| Application temperature | 10 - 35 °C (50 - 95 °F) | ||||
| Open time (CQP526-2) | 4 minutes A | ||||
| Peak exotherm time / temperature | 12 minutes / 110 °C (230 °F) A | ||||
| Shore D hardness (CQP023-1 / ISO 48-4) | 75 | ||||
| Tensile strength (ASTM D638) | 16 MPa (2300 psi) | ||||
| E-Modulus (ASTM D638) | elongation 0.1 - 1.0 % | 780 MPa (110 ksi) | |||
| Tensile lap-shear strength (CQP046-6 / ISO 4587) | 21 MPa (3050 psi) | ||||
| Service temperature (CQP513-1) | -40 - 80 °C (-40 - 176 °F) | ||||
| Shelf life | 9 months B |