3M(TM) Scotch-Weld(TM) Structural Plastic Adhesive DP8010 Blue, 490 mL, 6 per case
Product Info
71601 SCOTCH-WELD ACRYLIC ADHESIVE
3M(TM) Scotch-Weld(TM) Structural Plastic Adhesive DP8010 Blue, 490 mL, 6 per case
When using a Duo-Pak (DP) size adhesive, rely on 3M dispensing equipment for convenient and accurate metering, mixing and dispensing.
Creates a Strong Bond on Low Surface Energy Plastics
Structural bonds can be achieved without special surface treatments such as chemical etching, plasma, flame, or corona treatment or priming. Simply wipe the surfaces with isopropanol to remove mold release agents, dust dirt, etc. 3M™ Scotch-Weld™ Structural Plastic Adhesive DP8010 Blue also bonds metals, ceramics, and wood and most other plastics. It is slightly flexible when cured. We also formulate this adhesive with 8 mil spacer beads for bond line spacing.
Recommended Applications
- Joining plastics to metals, such as in the manufacture or repair of appliances
- Bonding low surface energy plastics without priming
- Impact resistance composite bonding
- Manufacture or repair of various sporting goods equipment
- Low surface energy plastics such as polypropylene, polyethylene and thermoplastic elastomers (TPEs)
Our 3M™ Scotch-Weld ™ Acrylic Adhesive DP8010 starts with medium viscosity for controlled dispensing and spreads to sufficiently wet out the surface. The mix ratio is 10:1 and provides a 10 minute work life. The adhesive reaches handling strength in approximately 1 hour and is fully cured in 8-24 hours (at 72° F /22° C).
Easy Adhesion with Acrylic
Acrylic adhesives are two-part adhesives that provide excellent bond strength and durability. Often referred to as epoxy adhesives or epoxy glue, acrylics actually belong to a separate chemical family with their own unique characteristics. This very unique adhesive bonds LSE plastics without priming or other surface treatments.
- Creates strong bond on low surface energy plastics (LSE) such as polyolefin with minimal or no surface prep required
- Resists many chemicals, water, humidity and corrosion
- Formulated to bond multi-material assemblies such as LSE plastics, thermoplastics, composites and metals
- Medium viscosity allows controlled dispensing
- 10 minute work life with 60 minute handling strength
- Strong adhesive can replace screws, rivets and welding
Adhesive Type | Acrylic |
Application | - Small Joint Assembly - Bonding Composite Materials - Panel to Frame/Stiffner to Panel Assembly - Sealing, Potting and Encapsulating - Mounting and Trim Attachment |
Color Family | Blue |
Container Size (Imperial) | 16.57 fl oz (US) |
Container Size (Metric) | 490 ml |
Design Challenges | Noise Vibration & Harshness Control NVH |
Full Cure Time | 8-24 Hours @ 72 F (22 C) |
Hardness | 55-60 Shore D |
Indoor/Outdoor | Both |
Maximum Operating Temperature (Celsius) | 66 Degree Celsius |
Maximum Operating Temperature (Fahrenheit) | 250 Degree Fahrenheit |
Open Time | 10 Minute |
Physical Form | Flowable Liquid |
Product Color | Blue |
Product Form | Cartridge |
Product Key | DP8010 |
Product Number | 8010 |
Product Type | Acrylic Adhesive |
Set Time | - 10 Minute - 60 Minute |
Shear Strength | 2700 psi |
Specific Gravity | 1.01 |
Storage Temperature | <=40 Degree Fahrenheit |
Storage Temperature (Celsius) | 4 °C |
Substrate | - Paint - Wood - Glass - HSE Plastics and Glass - Wood & Hardboard - Plastics (ABS, PVC, Acrylic) - Plastics (High Performance Nylon) - Glass & Ceramics - Plastics (Polyolefins and Thermoplastic Elastomers) - Metal (Painted) - LSE Plastics - Plastics: HSE, MSE (ABS, Acrylic, Polycaronate, Nylon) - Ceramic - Plastics: LSE (Polypropylene, Polyethylene) - Paints (Powder Coat, Painted Metal, Composite Panel) - Smooth - Metal (Unpainted) - Metal - Stone |
Substrate 1 | - Smooth - Glass - Wood - Metal - Plastics (Polyolefins and Thermoplastic Elastomers) - LSE Plastics - Paint - Plastic, Easy-to-Bond (HSE) - Glass & Ceramics - Plastics (High Performance Nylon) - Wood & Hardboard - Plastics (ABS, PVC, Acrylic) - Plastics (Flexible Vinyl) - Plastic, Hard-to-Bond (LSE) - Epoxy - Fiber Reinforced - Painted Surface, Hard-to-Bond (LSE) - Thermoplastics - Thermosets - Fiber Reinforced - Nylon - Fiber Reinforced - Engineered Thermoplastics - Polypropylene |
Substrate 2 | - Paint - Smooth - Wood - HSE Plastics and Glass - Glass & Ceramics - Plastics (Polyolefins and Thermoplastic Elastomers) - LSE Plastics - Plastics (ABS, PVC, Acrylic) - Wood & Hardboard - Glass - Metal - Plastics (High Performance Nylon) - Painted Surface, Hard-to-Bond (LSE) - Plastic, Hard-to-Bond (LSE) - Thermoplastics - Nylon - Fiber Reinforced - Engineered Thermoplastics - Plastics (Flexible Vinyl) - Thermosets - Fiber Reinforced - Epoxy - Fiber Reinforced - Polypropylene - Ceramic - Plastics: HSE, MSE (ABS, Acrylic, Polycaronate, Nylon) - Plastics: LSE (Polypropylene, Polyethylene) - Metal (Painted) - Metal (Unpainted) - Stone - Paints (Powder Coat, Painted Metal, Composite Panel) |
Viscosity | Self-Leveling |
Viscosity Range (cps) at Room Temperature | - Base: 27,000, Accelerator: 17,000 – 40,000 - 20,000 |
Volume (Imperial) | 17.24 fl oz |
Work Time | 8 Minutes |
ECCN | EAR99 |
Item Specifications
-
EPOXY ACRYLIC AND URETHANE ADHESIVES
-
1.68 lbs per EA